Fa'amatalaga Puupuu:

O le gaosiga autu o meafaitino mata o le RP 350mm malosi masani graphite electrode o le suauʻu coke, lea e mafai ona faatagaina 13500-18000A i le taimi nei e ala i, faʻatagaina le gafatia gafatia o le itiiti ifo i le 14 ~ 18A / cm² density i le taimi nei, lea e masani ona faʻaaogaina i le faia o uʻamea, faia o le silikoni. , phosphorus samasama ma isi ogaumu malosi arc masani.


Fa'amatalaga Oloa

Faailoga o oloa

O oloa a Hexi ua pasia le ISO9001 quality management system certification ma maua ai le fa'atauina atu o le graphite electrode fa'atagaina e le malo o Saina.Faʻatasi ai ma le lelei lelei ma le sili atu ona lelei le faʻatau atu, o matou oloa o loʻo manaʻomia tele i le maketi o le lalolagi.

Fa'atusatusaga Fa'amatalaga Fa'apitoa mo le RP Graphite Electrode 14″
     
Electrode
Aitema Vaega Fa'asoa Fa'amatalaga
Uiga masani ole Pole
Taiala Igoa mm 350
Max Tatami mm 358
Min Diamita mm 352
Numera Umi mm 1600/1800
Max Umi mm 1700/1900
Min Umi mm 1500/1700
Ole tele ole Density g/cm3 1.55-1.63
malosi felavasai MPa ≥8.5
Young' Modulus GPa ≤9.3
Tetee Faapitoa µΩm 7.5-8.5
Tulaga maualuga o lo'o iai nei KA/cm2 14-18
Gafatia o lo'o iai nei A 13500-18000
(CTE) 10-6 ℃ ≤2.4
mea e lefulefu % ≤0.3
     
Uiga masani ole susu (4TPI/3TPI)
Ole tele ole Density g/cm3 ≥1.74
malosi felavasai MPa ≥16.0
Young' Modulus GPa ≤13.0
Tetee Faapitoa µΩm 5.8-6.5
(CTE) 10-6 ℃ ≤2.0
mea e lefulefu % ≤0.3


350-2
350-3350-4

Graphitization e faasino i le vevela vevela faagasologa togafitiga o le liua amorphous carbon i tolu-dimensional oka planar hexagonal mesh laminated graphite e faavevela oloa carbon i le 2300 ℃ po o luga i se ogaumu eletise maualuga vevela.O le graphitization o mea carbon e faia i se vevela maualuga o le 2300 ~ 3000 ℃.Talu ai ona o le faʻavevelaina o suauʻu faʻasolosolo e faigata ona maua se maualuga maualuga, e naʻo le faʻavelaina o le faʻavevela eletise e mafai ona ausia i totonu o pisinisi.